Overview of the main features of aluminium
Numerical nomination of aluminium and its alloys according to EN-AW
Technical features of the sheets
Chemical features of the sheets
Technical features of extruded sections
Chemical features of the extruded sections



  Overview of the main features of aluminium

  the aluminium is the most used metal after steel. In the nature, we can find it in the form of oxide A12 O3, extracted from "bauxite ore ".

 
Relative density (30% steel) 2,7 g/cm³
Stretchmodule N/mm˛ (30% steel) - E 69000N / mm²
Coefficient of linear thermal expansion -alpha 23,4 .10 exp(-6) / 1 K
Electric conductivity 20,35 m / omega.m.m²
Electric resistivity - ro 0,030 omega.m.m² / m
Thermic conductivity -lamda 170 - 220 W / mK
Specific heat - c 900 J / Kg K
Melting point - Tsm 580-660 °C
Atomic mass 27
Atomic number 13


 

Numerical nomination of aluminium and its alloys according to EN-AW


 
The first number refers to the type of alloy
1xxx aluminium 99,00% or more 4xxx aluminium silicium (Si) 7xxx aluminium zink (Zn)
2xxx aluminium copper (Cu) 5xxx aluminium magnesium (Mg) 8xxx other alloys
3xxx aluminium manganese (Mn

 6xxx aluminium magnesium           
          and silicium (Mg, Si)
 

 
The two last numbers indicates the minimum aluminium content
for example : EN-AW 1050 : minimum 99,5% aluminium)


  Mettalurgical states are indicated as follows :

Basic metallurgical states
F
 crude fabrication without limit specification about mecanical fertaures
O
 annealed
O1
 annealed at high temperature and slowly cooled
O2
 thermal treatment during the mecanical conversion
O3
 homogenized
H

 cold hammered after annealed or after hot treatment or combination of a cold hammering with a partial annealing or a stabilization annealing

The first number refers to the process
H1x

 only cold hammered in order to obtain the mecanical resistance H2x

 cold hammered beyond wished final quantity then annealed
H3x

 cold hammered and stabilized ( usually in order to improve the ductility) H4x

 cold hammered then lacquered in oven   
                                

 
The second number indicates :
H - x2 = 1/4 hard    H - x4 =1/2 hard    H - x6 = 3/4 hard    H - x8 = 4/4 hard    H - 19 = extra hard

Thermal treatment
T1 cooled after hot conversion and ripe T6 dissolved and then tempered
T2

 colled after hot conversion, cold hammering and ripe T7

 dissolved and sur-venu/stabilized
T3

 dissolved, cold hammered and ripe

T8

 dissolved, cold hammered and then tempered
T4

 dissolved and ripe

T9

 dissolved, cold hammered and then tempered
T5 colled after hot converstion and cold hammered    


  Technical features of the sheets

ISO / DIN

 EN inter.

 Inter.
state		 State

 Description

 RmN/mm²
Break
Rp 0,2
stretch.
      A50
      % 		Brinell HB
Hardness
Al 99,5 1050A H111 W 7
Annealing
65
20
20
22
Al 99,5 1050A H 112 F 8
Rew
75
30
20
22
Al 99,5 1050A H 12/22 F/G 9
1/4 Hard
85
65
7
30
Al 99,5 1050A H 14/24 F/G 11
1/2 Hard
105
85
4/5
35
Al 99,7 1070A H 14/24 F/G 11
1/2 Hard
105
85
4/5
35
Al 99,8 1080A H 14/24 F/G 11
1/2 Hard
105
85
4/5
35
Al 99,0 1200A H 14/24 F/G 11
1/2 Hard
105
85
4/5
35
Al 99,85 1085 H 18  
 
 
 
 
 
Al Cu Mg 1 2017A T 451 F 39
Tempered
385
245
9/13
100
       
 
 
 
 
 
Al Mn Cu 3003 H 44 H 44
1/2 Hard
145
115
4/6
44
Al Mn 1 3103 H 44 H 44
1/2 Hard
185
155
2
58
Al Mn1Mg0,5 3005 H42 H42
1/2 Hard
170
130
4
45
       
 
 
 
 
 
Al Mg 1 5005 H 14/24 F/G 15
1/2 Hard
145
120
2/3
48
Al Mg 2,5 5052 H 112 W 17
Annealing
170
70
7
50
Al Mg 4,5 Mn 5083 H 111 W 28
Annealing
275
125
17
70
Al Mg 4    Mn 5086 H 111 W 28
Annealing
240
100
18
65
Al Mg 3 5754 H 111 W 19
Annealing
190
80
14/18
52
Al Mg 3 5754 H 14/24 F/G 24
1/4 Hard
190
80
14/18
73
Al Mg 3 5754 H 12/22 F/G 22
1/2 Hard
220
170
7/10
66
       
 
 
 
 
 
Al Mg Si 1 6082 T651 F 30
TemperedA
275
230
6/10
90


  Chemical features of the sheets

ISO / DIN

 EN inter.
 Inter.
state 		State

     Si

    Fe

     Cu

    Mn

    Mg

      Cr

   Zn

          Ti
   
Al 99,5 1050A H111 W 7
0,25
0,4
0,05
0,05
0,05
-
0,07
<0,10
Al 99,5 1050A H 112 F 8
0,25
0,4
0,05
0,05
0,05
-
0,07
<0,10
Al 99,5 1050A H 12/22 F/G 9
0,25
0,4
0,05
0,05
0,05
-
0,07
<0,10
Al 99,5 1050A H 14/24 F/G 11
0,25
0,4
0,05
0,05
0,05
-
0,07
-
Al 99,7 1070A H 14/24 F/G 11
0,20
0,25
0,04
0,03
0,03
-
0,04
-
Al 99,8 1080A H 14/24 F/G 11
0,15
0,15
0,03
0,02
0,02
-
0,03
<0,02
Al 99,0 1200A H 14/24 F/G 11
Si+Fe<
0,95
0,05-0,2
0,05
-
-
0,10
<0,05
Al 99,85 1085 H 18  
0,10
0,12
0,03
0,02
0,02
-
0,03
<0,02
Al Cu Mg 1 2017A T 451 F 39
0,2-0,8
0,70
3,5-4,5
0,4-1,0
0,4-1,0
0,10
0,25
-
       
 
 
 
 
 
 
 
 
Al Mn Cu 3003 H 44 H 44
0,6
0,70
0,05-0,2
1,0-1,5
-
-
0,10
-
Al Mn 1 3103 H 44 H 44
0,6
0,70
0,05-0,2
1,0-1,5
0,30
0,10
0,10
<0,10
Al Mn1Mg0,5 3005 H42 H42
0,6
0,70
0,30
1,0-1,5
0,2-0,6
0,10
0,25
<0,10
       
 
 
 
 
 
 
 
 
Al Mg 1 5005 H 14/24 F/G 15
0,30
0,70
0,20
0,20
0,5-1,1
0,10
0,25
-
Al Mg 2,5 5052 H 112 W 17
0,25
0,40
0,10
0,10
2,2-2,8
0,15-0,3
0,10
-
Al Mg 4,5 Mn 5083 H 111 W 28
0,40
0,40
0,10
0,4-1,0
4,0-4,9
0,05-0,2
<0,15
<0,15
Al Mg 4    Mn 5086 H 111 W 28
0,40
0,50
0,10
0,4-1,0
4,0-4,9
0,05-0,2
0,155
-
Al Mg 3 5754 H 111 W 19
0,40
0,40
0,10
0,50
2,6-3,6
0,30
0,20
<0,15
Al Mg 3 5754 H 14/24 F/G 24
0,40
0,40
0,10
0,50
2,6-3,6
0,30
0,20
0,15
Al Mg 3 5754 H 12/22 F/G 22
0,40
0,40
0,10
0,50
2,6-3,6
0,30
0,20
0,15
       
 
 
 
 
 
 
 
 
Al Mg Si 1 6082 T651 F 30
0,7-1,3
0,50
0,10
0,4-1,0
0,6-1,2
0,25
0,20
0,10


  Technical features of the extruded sections

ISO / DIN

 EN inter.

 Inter.
state 		State

 Description

 RmN/mm²
Break.
   Rp 0,2
  Stretch.
     A50
       % 		Brinell HB
Hardness
Al Mg Si 0,5 6060 T 3 F 13
TemperedA
130
85
6
45
Al Mg Si 0,5 6060 T 4 F 18
TemperedA
185
150
10
60
Al Mg Si 0,5 6060 T 5 F 22
TemperedA
215
160
12
70
Al Mg Si 0,5 6063 T 66 F 22
TemperedA
215
160
6/10
75
Al Mg Si 1 6082 T 3 F 15
TemperedA
250
200
10
35
Al Mg Si 1 6082 T 6 F 32
TemperedA
310
260
10
95
Al Mn Si Pb 6012 T 6 F 28
TemperedA
310
260
10
80
Al Mg 4,5 Mn 5083 H 111 F 7/22
Annealing
275
125
17
70
Al Cu Mg Pb 2007 T 4 F 17/22
TemperedA
280
210
10
-
Al Cu Mg Pb 2007 T 4 F 35
TemperedA
280
210
10
100
Al Cu Mg Pb 2007 T 3 F 37
TemperedA
280
210
10
100
Al Cu Bi Pb 2011 T 3  -
TemperedA
280
210
10
-
Al Cu Bi Pb 2011 T 6  -
TemperedA
295
195
6/8
-
Al Cu Mg 1 2017A T 4 F 22
TemperedA
385
245
9/13
140
AlZnMgCu1,5 7075 T 6 F 35
TemperedA
280
210
10
140


  Chemical features of the sections

ISO / DIN

 EN inter.
 Inter.
state 		State

     Si

    Fe

    Cu

    Mn

    Mg

     Cr

    Zn

     Ti
  
Al Mg Si 0,5 6060 T 3 F 13
0,3-0,6
 0,1-0,3 0,10 0,10
0,35-0,6
0,05
0,15
<0,1
Al Mg Si 0,5 6060 T 4 F 18
0,3-0,6
 0,1-0,3 0,10 0,10
0,35-0,6
0,05
0,15
<0,1
Al Mg Si 0,5 6060 T 5 F 22
0,3-0,6
 0,1-0,3 0,10 0,10
0,35-0,6
0,05
0,15
<0,1
Al Mg Si 0,5 6063 T 66 F 22
0,3-0,6
 0,1-0,3 0,10 0,10
0,35-0,6
0,05
0,15
<0,1
Al Mg Si 1 6082 T 3 F 15
0,7-1,3
 0,50 0,10 0,4-1,0
0,6-1,2
0,25
0,20
<0,1
Al Mg Si 1 6082 T 6 F 32
0,7-1,3
 0,50 0,10 0,4-1,0
0,6-1,2
0,25
0,20
<0,1
Al Mn Si Pb 6012 T 6 F 28
0,7-1,3
 0,50 0,10 0,4-1,0
0,6-1,2
0,25
0,20
<0,2
Al Mg 4,5 Mn 5083 H 111 F 7/22
0,80
 0,40 0,10 0,4-1,0
4,0-4,9
0,05-0,2
0,155
-
Al Cu Mg Pb 2007 T 4 F 17/22
0,80
 0,70 4,0-6,0 Bi+Pb
-
0,10
0,30
0,2
Al Cu Mg Pb 2007 T 4 F 35
0,80
 0,70 4,0-6,0 Bi+Pb
-
0,10
0,30
0,2
Al Cu Mg Pb 2007 T 3 F 37
0,40
 0,70 4,0-6,0 Bi+Pb
-
0,10
0,30
0,2
Al Cu Bi Pb 2011 T 3  -
0,40
 0,70 5,0-6,0 Bi+Pb
-
-
0,30
-
Al Cu Bi Pb 2011 T 6  -
0,40
 0,70 5,0-6,0 Bi+Pb
-
-
0,30
-
Al Cu Mg 1 2017A T 4 F 22
0,2-0,8
 0,70 3,5-4,5 0,4-1,0
0,4-0,8
0,10
0,25
-
Al ZnMgCu1,5 7075 T 6 F 35
0,40
 0,50 1,2-2,0 0,30
2,1-2,9
0,2-0,36
5,1-6
-